Stress Relaxation Aging Behavior of AA2219 Subjected to Large Pre-Strain at Room Temperature
Forum | 更新时间：2026-10-09

    • Stress Relaxation Aging Behavior of AA2219 Subjected to Large Pre-Strain at Room Temperature

    • Aeronautical Manufacturing Technology   Vol. 69, Issue 18, (2026)

    • DOI：10.16080/j.issn1671-833x.26010050    

      CLC： V26;TG166

    • Received：03 April 2026，

      Revised：2026-05-05，

      Accepted：28 June 2026，

      Published：15 September 2026

    移动端阅览

  • SHI Jiaai, XU Kekun, LI Dechong, et al. Stress relaxation aging behavior of AA2219 subjected to large pre-strain at room temperature[J]. Aeronautical Manufacturing Technology, 2026, 69(18): 26010050. DOI： 10.16080/j.issn1671-833x.26010050.

  •  
  •  

0

Views

4

下载量

0

CSCD

Alert me when the article has been cited
提交
Tools
Download
Export Citation
Share
Add to favorites
Add to my album

Related Articles

Regulation of Interfacial Microstructural Evolution and Mechanical Response Mechanisms of Ti/Al/Mg Clad Plates via Rolling Reduction Ratio
Mechanical Behavior and Microstructure Evolution of TA16 Titanium Alloy During Electrically-Assisted Plastic Deformation
Study on Splicing and Reinforcement Process for Carbon Fiber Panel/Aluminum Honeycomb Sandwich Panels
Effect of Feed Ratio on Microstructure Evolution and Mechanical Properties of 2219 Aluminum Alloy by Additive Friction Stir Deposition
Microstructures and Mechanical Properties of Wire-Based Friction Stir Additive Manufacturing for 2195 Al–Li Alloys

Related Author

WEI Junxin
LI Xiaojie
GUO Miao
WU Jiejie
HAN Jianchao
XI Shuaiying
FEI Yanhan
LIU Yuan

Related Institution

College of Mechanical Engineering, Taiyuan University of Technology
Engineering Research Center of Advanced Metal Composites Forming Technology and Equipment of Ministry of Education, Taiyuan University of Technology
National Key Laboratory of Metal Forming Technology and Heavy Equipment
China Special Equipment Inspection and Research Institute
Dalian Changfeng Industrial Corporation
0