碳纤维增强复合材料铣削加工表层损伤演化研究

周井文; 潘华东

doi:10.16080/j.issn1671-833x.2017.23/24.103

您当前的位置：

首页 >

文章列表页 >

碳纤维增强复合材料铣削加工表层损伤演化研究

学术论文 | 更新时间：2025-10-30

- 碳纤维增强复合材料铣削加工表层损伤演化研究
- 航空制造技术 2017年60卷第23/24期
- 作者机构：
  
  上海航天精密机械研究所,上海,201600
- 作者简介：
- 基金信息：
- DOI：10.16080/j.issn1671-833x.2017.23/24.103
  中图分类号：
- 纸质出版：2017
- 稿件说明：
移动端阅览
周井文1，潘华东1，杨叶1，杨斌1，陈燕2. 碳纤维增强复合材料铣削加工表层损伤演化研究[J]. 航空制造技术, 2017, 60(23/24): 103-108. ZHOU Jingwen1, PAN Huadong1, YANG Ye1, YANG Bin1, CHEN Yan2. Research on Damage Evolution of Skin Layer During Trimming of CFRP. Aeronautical Manufacturing Technology, 2017, 60(23/24): 103-108.

ZHOU Jingwen, PAN Huadong. Research on Damage Evolution of Skin Layer During Trimming of CFRP[J]. Aeronautical Manufacturing Technology, 2017, 60(23/24).
周井文1，潘华东1，杨叶1，杨斌1，陈燕2. 碳纤维增强复合材料铣削加工表层损伤演化研究[J]. 航空制造技术, 2017, 60(23/24): 103-108. ZHOU Jingwen1, PAN Huadong1, YANG Ye1, YANG Bin1, CHEN Yan2. Research on Damage Evolution of Skin Layer During Trimming of CFRP. Aeronautical Manufacturing Technology, 2017, 60(23/24): 103-108. DOI： 10.16080/j.issn1671-833x.2017.23/24.103.

ZHOU Jingwen, PAN Huadong. Research on Damage Evolution of Skin Layer During Trimming of CFRP[J]. Aeronautical Manufacturing Technology, 2017, 60(23/24). DOI： 10.16080/j.issn1671-833x.2017.23/24.103.

摘要

通过引入工件倾角的定义，采用PCD 立铣刀对CFRP 层压板材料进行切边试验，并对加工过程中的铣削力进行测量，对加工表层不同缺陷形式进行观察分类。研究了不同表层纤维方向、工件倾角和刀具进给量对CFRP 表层的缺陷形式和演化规律。结果表明：CFRP 层压板铣削表层缺陷主要可以分为崩边、毛刺、撕裂和分层缺陷，其中表层撕裂缺陷是最主要的缺陷形式；刀具进给量是影响表层缺陷，尤其是撕裂缺陷形成和发展的最主要的因素；垂直于铺层平面的切削分力直接影响表层缺陷演变与转化。

Abstract

Polycrystalline diamond (PCD) end mill was applied during the trimming experiment of CFRP by introducing the definition of workpiece inclined angle. The milling forces were recoded and different types of machining defects were observed at the same time. The influences of carbon fiber angle

workpiece inclined angle and feed rate on the types and evolution of machining defects were analyzed. The results show that the main machining defect is avulsion of carbon fiber bundles with small amount of chipping

burrs and delamination. The feed rate of cutter is the most significant factor on the occurrence of machining defects especially on the avulsion of fiber bundles. The cutting force perpendicular to the laminate panel has the direct influence on the occurrence and evolution of defects.

关键词

Keywords

references

浏览量

142

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

热压罐成型典型制造缺陷对复合材料的力学性能影响研究

碳纤维增强树脂基复合材料钻削缺陷研究进展

CFRP螺旋铣孔加工中的轴向力抑制方法

复合材料夹芯结构的数字化敲击检测技术研究

利用交变旋转磁场去除叶片气膜孔毛刺的试验研究*