超细晶WC–10%Co硬质合金三刃刀具放电等离子烧结工艺研究

王国峰; 刘青; 石文展; 李丹峰

doi:10.16080/j.issn1671-833x.2020.03.086

您当前的位置：

首页 >

文章列表页 >

超细晶WC–10%Co硬质合金三刃刀具放电等离子烧结工艺研究

研究论文 | 更新时间：2026-04-17

- 超细晶WC–10%Co硬质合金三刃刀具放电等离子烧结工艺研究
- 航空制造技术 2020年63卷第3期页码：86-91
- 作者机构：
  
  哈尔滨工业大学材料科学与工程学院,哈尔滨,150001
- 作者简介：
- 基金信息：
- DOI：10.16080/j.issn1671-833x.2020.03.086
  中图分类号：
- 纸质出版：2020
- 稿件说明：
移动端阅览
王国峰，刘青，石文展，李丹峰. 超细晶WC–10%Co硬质合金三刃刀具放电等离子烧结工艺研究[J]. 航空制造技术, 2020, 63(3): 86-91.

WANG Guofeng, LIU Qing, SHI Wenzhan, LI Danfeng. Investigation on Spark Plasma Sintering Process of Ultra-Fine Grained WC–10%Co Cemented Carbide Three-Edged Tool. Aeronautical Manufacturing Technology, 2020, 63(3): 86-91.
王国峰，刘青，石文展，李丹峰. 超细晶WC–10%Co硬质合金三刃刀具放电等离子烧结工艺研究[J]. 航空制造技术, 2020, 63(3): 86-91. DOI： 10.16080/j.issn1671-833x.2020.03.086.

WANG Guofeng, LIU Qing, SHI Wenzhan, LI Danfeng. Investigation on Spark Plasma Sintering Process of Ultra-Fine Grained WC–10%Co Cemented Carbide Three-Edged Tool. Aeronautical Manufacturing Technology, 2020, 63(3): 86-91. DOI： 10.16080/j.issn1671-833x.2020.03.086.

摘要

利用真空放电等离子烧结技术实现了超细晶 WC–10%Co 硬质合金块体材料的制备，研究了烧结温度和保温时间对硬质合金微观组织和力学性能的影响规律。试验结果表明：当烧结温度从 1200℃ 升高至 1350℃ 时，硬质合金的致密度和维氏硬度均逐渐增大；在 1350℃，保温时间从 3min 延长至 9min 时，硬质合金的致密度和维氏硬度均先增大后减小。在烧结温度为 1350℃，保温时间为 6min 时，致密度最高为 99.3%，维氏硬度为 2212HV。在 1350℃、轴向压力 30MPa、保温 6min 最佳烧结工艺参数下，制备了高质量复杂形状硬质合金三刃刀具，刀具致密度为 99.2%，硬度为 2232HV

Abstract

The effect of sintering temperature and holding time on the microstructures and mechanical properties of WC–10%Co cemented carbide during spark plasma sintering process was investigated. The results indicated that the densities and hardness were enhanced with the increase of sintering temperature from 1200℃ to 1350℃. The densities and hardness enhanced first and then decreased with the increase of holding time from 3min to 9min at 1350℃. The density of cemented carbide arrived maximum value of 99.3%

as well as the hardness of 2212HV at the sintering parameters of 1350℃ and 6min. The three-edged tool with high quality was sintered at the optimum parameters. The density and harness of the tool were 99.2% and 2232HV

respectively.

关键词

Keywords

references

浏览量

203

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

TC4合金热变形特性及变形参数对组织和性能的影响

TA15钛合金高压及中压电子束焊接接头组织性能研究

热处理对SPF/DB后钛合金组织及性能的影响

薄壁铝合金搅拌摩擦焊接头组织及性能

协同双面搅拌摩擦焊接技术