热处理对EBM Ti–4Al–5V–5Mo–6Cr–1Nb合金显微组织与拉伸性能的影响

乔虹; 刘运玺; 陈玮; 杨洋

doi:10.16080/j.issn1671-833x.2020.19.085

您当前的位置：

首页 >

文章列表页 >

热处理对EBM Ti–4Al–5V–5Mo–6Cr–1Nb合金显微组织与拉伸性能的影响

研究论文 | 更新时间：2025-10-30

- 热处理对EBM Ti–4Al–5V–5Mo–6Cr–1Nb合金显微组织与拉伸性能的影响
- 航空制造技术 2020年63卷第19期页码：85-90
- 作者机构：
  
  1. 中国航空制造技术研究院,北京,100024
  2. 高能束流加工技术重点实验室,北京,100024
- 作者简介：
- 基金信息：
- DOI：10.16080/j.issn1671-833x.2020.19.085
  中图分类号：
- 纸质出版：2020
- 稿件说明：
移动端阅览
乔虹，刘运玺，陈玮，杨洋. 热处理对EBM Ti–4Al–5V–5Mo–6Cr–1Nb合金显微组织与拉伸性能的影响[J]. 航空制造技术, 2020, 63(19): 85-90.

QIAO Hong,LIU Yunxi,CHEN Wei, YANG Yang. Effect of Heat Treatment on Microstructure and Tensile Properties of EBM Ti–4Al–5V–5Mo–6Cr–1Nb Alloy. Aeronautical Manufacturing Technology, 2020, 63(19): 85-90.
乔虹，刘运玺，陈玮，杨洋. 热处理对EBM Ti–4Al–5V–5Mo–6Cr–1Nb合金显微组织与拉伸性能的影响[J]. 航空制造技术, 2020, 63(19): 85-90. DOI： 10.16080/j.issn1671-833x.2020.19.085.

QIAO Hong,LIU Yunxi,CHEN Wei, YANG Yang. Effect of Heat Treatment on Microstructure and Tensile Properties of EBM Ti–4Al–5V–5Mo–6Cr–1Nb Alloy. Aeronautical Manufacturing Technology, 2020, 63(19): 85-90. DOI： 10.16080/j.issn1671-833x.2020.19.085.

摘要

研究了电子束选区熔化（EBM）Ti–45561 合金的显微组织及热处理对其组织性能的影响。发现成形态材料具有沿 z 方向外延生长的 β 柱状晶，这是由于凝固过程中的温度梯度造成的，而 730℃ 的成形腔温度环境使得每一个 β 晶粒内部有针状 α 相析出。在后续热处理过程中，随着时效温度的升高与时间的延长，晶界处析出的 α 相逐渐粗化并趋向于连续分布，晶界内的次生 α 相逐渐粗化；随着固溶温度的升高，初生 α 相的数量逐渐减少。在影响 EBM Ti–45561 合金强度与塑性的热处理参数中，时效温度的影响最大，固溶温度次之，时效时间的影响最小。随着时效温度升高，材料的强度下降而塑性增加。

Abstract

The effect of heat treatment on microstructure and tensile properties of EBM Ti–45561 was investigated. The as-build material exhibited columnar β grains epitaxially grew along z direction

which is caused by the temperature gradient during the solidification process. Acicular α phase precipitated inside each β grains due to the 730℃ environment temperature. With the increase of post-build annealing temperature and extension of annealing time

the grain boundary α phase and secondary α phase were both coarsened. When the solution treat temperature was increased

the percentage of primary α phase decreased. Among the 3 heat treatment parameters

the annealing temperature has the strongest influence on tensile properties

and the annealing time has the smallest influence. The elongation of the EBM Ti–45561 increased with annealing temperature; while the strength of the material decreased with annealing temperature.

关键词

Keywords

references

浏览量

215

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

电子束熔丝成形TC17钛合金显微组织与拉伸性能研究

热处理对激光增材制造TC4ELI显微组织与拉伸性能的影响

背面焊缝激光重熔处理对Ti/Al高速FA–MIG焊接头组织性能的影响

激光立体成形钛合金角盒的组织与性能研究

近球形TC4钛合金粉末注射成形